CIPDB › China Industry › Tools & Hardware › Universal Hardware Parts
China, Chinese Custom Engine Isolation Mounts for Superior Vibration Dampening1 Industrial Products Supplier Manufacturer Details, price list catalog:
Universal Hardware PartsCustom MountPolyurethane Mount
Thermotest Technology (Suzhou) Co., Ltd.
Preview:
Product Description Product DescriptionMaterial: Mixed-celled PU elastomer (Polyurethane)Color: orangeDimensions can be customized,Other dimensions, punched and moulded parts on request.PRODUCT PROPERTIESCombination of spring and damping characteristicsElastic, versatile polyurethane materialMixed-cell pore structure ADVANTAGESHigh elasticity, long service lifeStatic range of use of 0.011 N/mm2 to 1.2 N/mm2Load peaks up to 6.0 N/mm2Very low amplitude dependenceProven long-term behaviourHigh fatigue strengthFinely graded range (10 standard types) for optimum system designAbility to provide customer-specific modifications Detailed Photos Product Parameters Range of use CompressiveDeformation Shape factor-dependent, the specified values apply to shape factor of q=3Static range of use (static loads)up to 0.018N/mm2approx. 7%Impact range of use (dynamic loads)up to 0.023N/mm2up to 20%Load peaks(occasional, brief loads)up to 0.75 N/MM2approx. 80%Technical Data Material Properties Test MethodsCommentMechanical loss factor0.23DIN 53513 1temperature-, frequency-, specific load- and amplitude-dependentRebound resilience40 %EN ISO 8307 1 Compression hardness 30.02N/mm2EN ISO 844 1at 10 % linear compression, 3rd load cycleCompression set 2< 5 %EN ISO 1856 150 % deformation, 23 °C, 72 h, 30 min after removal of loadStatic modulus of elasticity 30.08 N/mm2 at specific load of 0.018 N/mm2Dynamic modulus of elasticity 30.29N/mm2DIN 53513 1at specific load of 0.018 N/mm2, 10 HzStatic shear modulus0.06N/mm2 DIN ISO 1827 1at a pretension of 0.018 N/mm2Dynamic shear modulus0.12N/mm2DIN ISO 1827 1at a pretension of 0.018 N/mm2, 10 HzMin. tensile stress at rupture0.35 N/mm2DIN EN ISO 527-3/5/500 1 Min. tensile elongation at rupture230%DIN EN ISO 527-3/5/500 1 Abrasion 2≤ 400 mm3DIN IS O 464 9 1load 2.5 NCoefficient of friction (steel) 0.5Getzner Werkstoffedry, static frictionCoefficient of friction (concrete) 0.7Getzner Werkstoffedry, static frictionSpecific volume resistivity> 1010 Ω·cmDIN EN 6 2631-3-1 1dryThermal conductivity0.05 W/mKDIN EN 12 667 Temperature range -30 °C to 70 °C short term higher temperatures possibleFlammabilityclass EEN ISO 11925-2normal combustible, EN 13501-11Measurement/evaluation in accordance with the relevant standard2 The measurement is performed on a densitydependent basis with differing test parameters3 Values apply to shape factor q = 3 · Quasi-static load deflection curve measured with a loading rate of0.0018 N/mm2/s.· Testing between flat and plane-parallel steel plates, recording of 3rd load, with filtered starting range in accordance with ISO 844, testing at room temperature.· Shape factor q = 3· Quasi-static modulus of elasticity as tangential modulus from the load deflection curve. Dynamic modulus of elasticity from sinusoidal excitation at a vibration velocity of 100 dBv re. 5·10-8 m/s (corresponding to a vibration amplitude of 0.22 mm at 10 Hz and 0.08 mm at 30 Hz).· Measurement in accordance with DIN 53513· Shape factor q = 3· Natural frequencies of a vibratory system with a single degree of freedome, consisting of a mass and an elastic bearing made of Sylomer? SR 18 on a rigid surface.· Parameter: thickness of the Sylomer? bearing· Shape factor q = 3 · Reduction of the transmitted mechanical vibrations by implementation of an elastic bearing consisting of Sylomer? SR 18 based on a stiff subgrade.· Parameter: factor of transmission in dB, isolation rate in %
Purchasing Agent
Note: Send your message to supplier or manufacturer.
Welcome to our Professional and comprehensive procurement services...