CIPDB › China Industry › Metallurgy, Mineral & Energy › Steel & Products
China, Chinese AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow Bar1 Industrial Products Supplier Manufacturer Details, price list catalog:
China Products Details Supplier Manufacturer price list catalog
Steel ProductsHollow BarSteel Tube
Hunan Shunfu Metal Material Co., Ltd.
Preview:
Product Description AISI SAE 4330V Forged Q+T Boring/Drill Alloy Steel Hollow BarIntroduceWe are Chinese professional manufacturer of forged QT boring steel bar for oil services. We can supply multiple AISI/SAE standard alloy steel materials and forged bar diameter 80-500mm, boring hole diameter 10-250mm, max boring length 14 meters. Product advantageBoring one side: no step in the boring barHigh-tech Boring Equipment: Good Straightness and Roughness, Tiny Tolerance and RoundnessStable mechanical property in materials after QT processChemical component according to America standard 100%Ensure UT and drift test for each piecesCompany advantageWe have decades of produce experience in QT/Boring process and strict quality management system(ISO NQA 9001)We cooperated with several middle-east oil gas companies for many times and have API certificates.Our sales team are professional steel industry staff and exporter with fluent English.We accept variety convenient payment ways and the third parties inspection organization. SpecificationProduct NameForged QT Boring Alloy Steel Bar For Oil ServicesSpecificationAPI 5CT/5CP/6ASteel Grade4130, 4140, 4145, 4145H, 4330V, 4137, 4340ProcessHot Forged+QT+BoringForged Bar Diameter8-500mmBoring Hole Diameter10-250mmLengthMax14 metersInspectionSize, Chemical, Mechanical, UT, Drift Test, Low/High Temp. ImpactCertificateMTC, CO/FE/FA, BV/SGSMOQ1-5 tonsDelivery Time10-30 daysTrade ItemFOB CIF CFR PPU PPDPackagingLoose/Bundle/Wooden Pallet/Wooden Box/Plastic Cloth Wraps /Plastic End Caps/Beveled ProtectorIntroduce AISI 4330V MOD is a modification of the 4330 alloy steel grade, with hardenability and other characteristics improved by the addition of vanadium. Alloy Steel 4330V offers good formability which is used for those that require a good combination of strength and impact resistance.Applications Shock loading or stress concentration applications are suited to this steel specification. 4330V is widely used in the oil and gas industry for applications such as oil tools, drill jars and shoes, tool holders and reamers and in the aerospace industry for applications such as bolting and air frames.Standards AMS 6427, AMS 6359, AMS 6304, ASTM A646, API 7 Specification Chemicals Composition GradeCMn maxSi maxCrMoNiP maxS maxV4330V0.2-0.301.00.800.40-0.600.30-0.501-1.50.0250.0100.05-0.10Mechanical Properties Yield strength Rp0.2,MPaTensile strength Rm,MPaElongation[%]Hardness[HBW]Impact, Charpy-V, -20oC[J] 1034 1138 15 341-388 32Heat Treatment Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities.AnnealingHeat the steel slowly to 820-860°C and allow enough time for the steel to be thoroughly heated. Cool slowly in the furnace to 580°C followed by air cooling.Stress Relieving When parts are heavily machined, ground or otherwise subject to cold work, stress relieving will be beneficial prior to hardening.Hardening 4330V steel is usually supplied ready heat treated to 35-39 HRc. If further heat treatment is required annealed 4330V should be heated slowly to 840-875°C and after adequate soaking at this temperature quench in oil. Temper as soon as the tools reach room temperature.Tempering Heat carefully to a suitable temperature selected by reference to a tempering chart or table, soak at the temperature for 2 hours per 25mm of ruling section, then allow to cool in air.Forging Preheat the steel carefully, then raise the temperature to 1070-1230°C for forging. Do not forge below 850°C. 4330V has good forging characteristics but care must be taken when cooling the steel due to its susceptibility to cracking. Cooling in ash or lime after forging is recommended.Machining Normalize and Temper at 1250°F(677°C) maximum prior to rough machine. This steel may also be machined at maximum strength, but machining must then be followed with a stress relieving at approximately 400°F(204°C).Weldability The steel has good welding characteristics and can be welded by resistance flash welding.Mill′s test certificate EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Purchasing Agent
Note: Send your message to supplier or manufacturer.
Welcome to our Professional and comprehensive procurement services...