CIPDB › China Industry › Metallurgy, Mineral & Energy › Aluminum
Aluminium Sheet Polished Aluminum Alloy Sheet Metal for Kitchen1
AluminumAluminum SheetAluminum Foil
Shanghai Zhongduo Aluminum New Material Group Co., Ltd.
Preview:
Product Description aluminium sheet Polished aluminum alloy sheet metal for kitchen utensilsAluminum sheet is any aluminum sheet metal thicker than foil but thinner than 6mm; it comes in many forms including diamond plate, expanded, perforated and painted aluminum sheet. Aluminum plate is any aluminum sheet metal that is thicker than 6mm.Supply aluminium hot/cold rolled coil/plate. Alloy: 1, 3, 5, 8 Series, high quality at competitive price.Aluminium alloy sheet1. Alloy: 1100, 1145, 1050, 1060, 1070, 3003 etc.2. Temper: H12. H14. H16. H18. H22. H24. H26. H32. H34. H36. H38. O etc.3. Thicknes: 0.2mm -- 5.0mm4. Width: Under1600mm5. Packing: Export standard, covering with brown paper and plastic film then packed with wooden case/pallet6. Origin: China7. Lead Time: Within 30 days8. Payment Terms: T/T, irrevocable L/C at sightRemarks: Specific requirement of alloy, temper or specification can be discussed at your request.1050 Aluminium alloy sheet belongs to commercially pure wrought family with a purity of 99.5% Aluminum. Except Al, 0.4% of Fe is added to 1050 aluminum alloy sheet , thus, it has high electrical conductivity. 1000 series aluminum group offers the best correction resistance compared to any alloy group, so does the 1050 aluminum alloy shee. haomei aluminum can reach this standard. For its simple processing technology, 1050 aluminum alloy shee is much cheaper comparing to other aluminum alloys plate and it is very commonly used in industry.Alloy 1100 aluminum sheet is highly resistant to chemical attack and weathering. It is a relatively soft alloy that is very formable and is used extensively in thin gauge and foil products. It has good welding characteristics and it is also used as a filler alloy for welding purposes.Alloy: 1100Temper: O, H111, H112, H12,H14, H16, H18, H22, H24, H26Thickness: 0.2mm--200mmWith: 500mm--2000mmLength: 1000mm--12000mmSurface: Mill finish, Bright finish, paper interleaved, one side film, both sides film. Chemical PropertiesAlloySiFeCuMnMgCrNiZnTiGaVOthersAluminiummin.EachTotal11000.95 Si+Fe0.05+0.20.05---0.1---0.050.15RemainderAluminum alloy 3003 sheet is a medium strength alloy with very good resistance to atmospheric corrosion and very good weldability as well as good cold formability. It has better mechanical properties, especially at elevated temperatures than the 1000 series alloys.Alloy: 3003Temper: O, H111, H112, H12,H14, H16, H18, H22, H24, H26Thickness: 0.2mm--200mmWith: 500mm--2000mmLength: 1000mm--12000mmSurface: Mill finish, Bright finish, paper interleaved, one side film, both sides film.Chemical PropertiesAlloySiFeCuMnMgCrNiZnTiGaVOthersAluminiummin.EachTotal30030.60.70.05-0.21.0-1.5---0.10---0.050.15Remainder1060 aluminum alloy sheet is pretty similar to 1050 aluminum alloy with more than 0.1% of aluminum by weight. Both 1050 and 1060 aluminum alloy sheet of Mingtai Al. lives up to ISO standards, but they cover different ASTM standards. 1060 aluminum alloy sheet contains 0.05% cooper, thus, its conductivity is 55%. Besides, 1060 aluminum alloy sheet is relatively low strength, essentially pure aluminum alloy plate with many different tempers, such as O (annealed), H12, H14, H16, H18, etc. what's more, other aluminum sheet belonging to commercial pure wrought family are available, including 1050, 1070, 1100 and so on and so forth.AlloyTemperThicknessmmTensile StrengthRm/Mpa Min.Yield StrengthRp0.2/Mpa Min.Elongation% Min.Content(max)0.250.350.050.030.03-0.050.030.15Remain Alloy TemperSpecifiedTensilestrengthYieldstrengthElongation Thickness(in.)(ksi)(ksi)(%) 1060-O(annealed)0.006-0.0198.0-14.02.5Min15 0.020-0.050Min22 0.051-3.000Min25 1060-H12/1060-H220.017-0.05011.0-16.09.0Min6 0.051-2.000Min12 1060-H14/1060-H240.006-0.01912.0-17.010.0Min1 0.020-0.050Min5 0.051-1.000Min10 1060-H16/1060-H260.006-0.01914.0-19.011.0Min1 0.020-0.050Min4 0.051-0.162Min5 1060-H18/1060-H280.006-0.019Min16.0Min12.0Min1 0.020-0.050Min3 0.051-0.128Min4 1060-H1120.250-0.499Min11.0Min7.0Min10 0.500-1.000Min10.0Min5.0Min20 1.001-3.000Min9.0Min4.0Min25 Applications of 1060 Aluminum sheet1060 aluminum sheet is noted for its excellent welding characteristics and formability by cold or hot working with commercial techniques. It cannot be hardened by heat treatment but only from cold working. Tempers H12, H14, H16 and H18 are determined by the amount of cold working imparted into the alloy. Moreover, 1060 aluminum plate has good corrosion resistance as well as poor machine-ability, and its machine-ability can be improved in harder (cold working) tempers, such as H16 and H18. For its features above, 1060 platehas a vast application, such as electric and chemical equipment, railroad tank cars, etc.aluminum sheet metal comes in a variety of thicknesses and weights in many different grades. haomei aluminium offers heat treatable aluminum sheet grades, like the popular 6061 aluminum alloy, that can be used for commercial applications that require strength, corrosion resistance and machinability, as well as non-heat treatable grades when formability and weldability are priorities. Popular applications for aluminum sheet include fuel tanks, roofing, boat hulls and automobile parts. Available grades include 1100, 3003, 5052, 5086, 5454 and 6061.Packing:Packing: Export standard, covering with brown paper and plastic film then packed with wooden case/pallet
Purchasing Agent
Note: Send your message to supplier or manufacturer.
Welcome to our Professional and comprehensive procurement services...