CIPDB › China Industry › Packaging & Printing › Industrial Packaging Bag

100% Biodegradable Food Packaging Bag Flat Roll Eco Friend Shopping Carrier Bag¹

Preview:

Product Description Product DescriptionBiodegradable Food BagsFlat Bag on RollApplication:Fresh bag , home use , food/fruits/vegetables fresh bag/storage bag/freezer bag. Features:- 100% biodegradable & compostable- Point Breaking design- Service life: 10 months- Printing :1 color on one side- multi-use durable and convient to use- roll food grede safety plastic packaging storage bag- fresh-keeping bag - accept customized designProduct ParametersSize:Flat bag on rollSizeL x W (cm)Thickness(mic)Small20 x 30 18 or CustomizedMedium25 x 35 18 or CustomizedLarge30 x 40 18 or CustomizedDetailed PhotosMaterial used in manufacturing:For food grade , the main composition is PLA , and small percent is corn starch.Polylactic acid (PLA) can be completely decomposed into carbon dioxide (CO2) and water (H2O) under natural conditions. PLA can be made into film products with high transparency, good barrier properties, excellent processability and mechanical properities,and can be used for flexible packaging of fruits and vegetables. our materialPolylactic acid (PLA) can be completely decomposed into carbon dioxide (CO2) and water (H2O) under natural conditions after being discarded.Item No: YPRX-PLA01Molecular Formula: H-[OCHCH3CO]n-OHCAS NO: 26100-51-6Color: WhiteStandard: GB/T 29284-2012 ItemUnitResultMonomer content and D-content%≤0.3Densityg/cm3>1.24Particle Diametermm2Melt index (190oC/2.16kg)g/10min10Melt pointoC>165Tensile Strength at BreakMPa>45Elongation at break%<5Tensile ModulusGPa3.5Notch Impact StrengthkJ/m2>4HDT(0.45Mpa)oC>100Bending strengthMpa>70Transmittance%>95Degradation Rate%>95 PLA can be made into film products with high transparency, good barrier properties, excellent processability and mechanical properities, and can be used for flexible packaging of fruits and vegetables.PLA objects can be fabricated by 3D printing, casting, injection moulding, extrusion, machining, and solvent welding. ItemUnitPPGPPPETPLADensityg/cm30.9-0.911.04-1.091.3-1.41.25Melt Indexg/10min0.2-201.5-30--1-30Tensile strengthMPa29.6-35≥58.8≥60≥50Elongation%200-7001.0-2.530-70≥5Transmittance%85-8888-9290-9290-95PLA can be made into film products with high transparency, good barrier properties, excellent processability and mechanical properities, and can be used for flexible packaging of fruits and vegetables.PLA can form a weekly acidic environment on the surface of the product. It has a basis for antibacterial and antifungal. If other antibacterial agents are used in addition, it can achieve an antibacterial rate of more than 90%, and can be used for antibacterial packaging of products.PBSPolybutylene succinateItem No: YPRX-PBS01, YPRX-PBS02Molecular Formula: HO-(CO-(CH2)4-CO-O-(CH2)4-0)n-HCAS NO: 25777-14-4Standard: GB/T 30294-2013Color: Natural whiteRaw Material: BDO(1,24-butanediol) Succinic AcidApplication: injection molding tablewares and cutlery textile, fishing net, engineering components medical applications, etc.PBS is biodegradable and environment-friendly material. Our PBS has excellent mechanical properties, close to PP and ABS plastics; The heat resistance is good, the thermal deformation temperature is close to 100 centigrade, and the service temperature after modification can exceed 100 centigrade. NoItemUnitYPRX-PBS01YPRX-PBS021Density, 25oCStandard valueg/cm31.25Deviation+0.032Density, 25oCoC105-1163MFRStandard valueg/10min≤1010-20Deviation4Moisture%≤0.25Hydroxyl contentmol/t≤506Color valueL valueStandard value--≥75A valueNominal value--≤5Deviation+0.5B valueNominal value--≤11Deviation+17Breaking tensile strengthMpa≥25.08Tensile strain at breaking%≥1509Bending strengthMpa≥25.010Bending modulusMpa≥400PBS is widely used in packaging (including food packaging, cosmetic bottles, drug bottles), tableware, disposable medical supplies, agricultural film, pesticide and fertilizer slow-release materials, biomedical polymer materials and other fields. It can not only meet the demand through petrochemical products, but also produce natural renewable crop products such as cellulose, diary by-products, glucose, fructose and lactose through biological fermentation, so as to realize green circular production from nature and return to nature.PBATItem No: YPRX-PBAT01Molecular Formula: H-(O-(CH2)4-O-CO-(CH2)4-CO-)n-(O-(CH2)4-O-CO-C6H4-CO-)m-H)CAS NO: 55231-08-8Color: Natural whiteStandard: GB/T 32336-2015Raw Material: BDO(1,4-butanediol), PTA(terephthalic acid) Adipic Acid NoItemUnitValue1Density, 25oCg/cm31.23+0.032Melting Point, pmoC110-1453MFRg/10min2.5-4.54Moisture%≤0.15Hydroxyl contentmol/t≤506Color valueL valueStandard value--≥70A valueNominal value--≤5Deviation+1B valueNominal value--≤10Deviation+17Breaking tensile strengthMpa≥158Tensile strain at breaking%≥5009Bending strengthMpa≥310Bending modulusMpa≥3011Vicat softening point A50oC≥8012Ash content%≤0.1 PBAT (short for polybutylene adipate terephthalate) is a biodegradable random copolyme, specifically a copolyester of adipic acid, 1,4-butanediol and terephthalic acid(from dimethyl terephthalate).It is generally seen as a fully biodegradable alternative to low-density polyrthylene, having many similar properties including flexibility and resilience, which makes it ideal for blending with another biodegradable polymer, allowing it to be used for many similar uses such as plastic bags and wraps.MODIFIED MATERIALSModified MaterialFilm Blowing Grade YPMH-S200Film Blowing Grade PLA Modified MaterialPLA+PBAT+STARCHItem Code: YPMH-S200Recommended applicationShopping vest bag, wrist bag, roll bag, food preservation bag; Electronic product packaging film, household.Appliance packaging film, medical hygiene film, etc.Product characteristics1) Good coloring performance, stable melt strength, and can be directly processed into various films;2) It is usually light white or light yellow, has fragrance, is easy to be decomposed by microorganisms, and has natural antistatic property;3) Good heat stability of raw materials, good recyclability of leftover materials, high temparature and strong shear force;4) This product has low moisture content. It is vacuum packed and can be used after opening.Material properties ItemTest methodConditions for itemUnitResult[1]Melt flow rate1S0 1133190oC, 2.16kgg/10min4.0-7.0Density1S0 118323oCg/cm31.27-1.32Melting pointDSC--oC110-130[1]The above data are measured values, not guaranteed values.Processing parameters TemperatureTypical value[2]Reference rangeMelting temperature 120oC115-125oCTemperature of film blowing heating areaPosterior segment025oC120-130oCMiddle segment130oC125-135oCAnterior segment135oC130-140oCMould head temperature 135oC130-140oCUpper limit of processing temperature 180oC [2]The above data are typical values and aer only for reference. In the actual processing process, the parameters can be adjusted appropriately.Typical film properties[3] Characteristics[4]Test methodConditions for testingUnitTypical values[5]Tensile strength longitudinal/transverse1S0 52725oCMPa21/12Elongation at break longitudinal/transverse1S0 52725oC%250/600Dart impact1S0 7765-125oCg 150[3]Typical film are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;[5]The above data are typical values, not guaranteed values.Modified MaterialFilm Blowing Grade YPMH-M300Film Blowing Grade PLA Modified MaterialPLA+PBAT+STARCHItem Code: YPMH-M300Recommended applicationsShopping vest bag, wrist bag, roll bag, food preservation bags; packaging film for electronic products, packaging film for home appliances, medical sanitary films, etc.Product Features1) Independent corn tachnology, high product strength, more than 30% higher than the tensile strength of conventional commercial products;2) Good coloring performance, stable melt strength, and can be directly processed into various films;3) It is usually light white, fragrant, easy to be decomposed by microorganisms, and has natural antistatic property;4) The raw materials have good thermostability, good recyclability of leftover materials, and can withstand high temperature and strong shear force.Material properties ItemTest methodConditions for itemUnitResult[1]Melt flow rate1S0 1133190oC, 2.16kgg/10min3.0-6.0Density1S0 118323oCg/cm31.38-1.43Melting pointDSC--oC110-130[1]The above data are measured values, not guaranteed values.Processing parameters TemperatureTypical value[2]Reference rangeMelting temperature 125oC120-130oCTemperature of film blowing heating areaPosterior segment145oC140-150oCMiddle segment145oC140-150oCAnterior segment150oC140-150oCMould head temperature 150oC140-150oCUpper limit of processing temperature 190oC [2]The above data are typical values and are only for reference. In the actual processing process, the parameters can be adjusted appropriately.Typical film properties[3] Characteristics[4]Test methodConditions for testingUnitTypical value[5]Tensile strength longitudinal/transverse1S0 52725oCMPa17/13Elongation at break longitudinal/transverse1S0 52725oC%300/500Dart impact1S0 7765-125oCg 190[3]Typical films are produced by film blowing mechanism with the material YPMH-M300, film thickness is 28 microns;[4]The data are measured by the newly produced film and can not be used as the basis for judging material quality;[5]The above data are typical values, not guaranteed values.Product DisplayDAGRADATION PROCESSBiodegradable bags refer to plastic bags that can be completely degraded under specific conditions. They are usually made of biodegradable materials such as polylactic acid (PLA) and polyester (PBAT), which reduce their stability during production and make them easier to degrade in the natural environment without residues.Compared with ordinary plastic bags, biodegradable bags have the advantages of environmental protection and sustainability. The degradation process refers to the decomposition of polymer molecules into small molecules through microbial action, hydrolysis, oxidation, and other methods, ultimately forming natural substances such as carbon dioxide, water, and organic matter. The degradation products are carbon dioxide and water, which can be directly absorbed by plants in the soil, returned to the soil, or entered the general environment, and can be degraded without polluting the environment.FAQ1. Q: What's your main material?Our main materials are PLA,PBS,PBAT and Corn Starch. The materials are 100% Compostable and Biodegradable, they can be degraded into H20 and C20 completely.2. Q: What information should I let you know if I want to get a quotation?The size of the products (Length x Width), if your bag's have the gusset, also please provide the gusset size.We usually quote you within 24 hours after we get your inquiry. If you are in urgency to get the quotation,please call us or tell us in your mail, so that we could regard your inquiry in priority.3. Q: The printing: How many colors printing in 1 side or 2 sides?It will be very useful if you can provide your bag's picture. Of course, samples will be best.4. Q: What's your MOQ?Usually 1 tons each kind, the more the cheaper.5. Q: What is the bag size? You can measure the length, width and height of the goods that need to packing, we will help you calculate the required size of the bag. We do customized products, any size & any color we can make according to your requirement.6. Q: Can you design for me?According to your requirement, we can add your company logo, website, phone number or your ideas on the bag.... Any color is available. Our profession designer can make design it to for you for free.Welcome to contact with us for more details!

× More Keyword ..

× More Menu ..

×

Manufacturing & Processing Machinery

×

Industrial Equipment & Components

×

Tools & Hardware Products